Tha Hastelloy C2000 na sheòrsa ùr de alloy Ni-Cr-Mo. Stèidhichte air C4 alloy, tha susbaint cromium air a leasachadh, agus tha cuir a-steach copar gu mòr a ’leasachadh an aghaidh oxidation agus an comas truaillidh a bhith a’ lughdachadh meadhan an alloy. Tha Hastelloy C2000 an-dràsta na shreath de aloidhean le deagh fhilleadh corrach de H2SO4, ach chan eil an aghaidh creimeadh intercrystalline cho math ri C4 alloy
Alloy | C | Cr | Ni | Fe | Mo. | W | Cu | Si | Mn | P | S |
Hastelloy C-2000 | ≤0.01 | 22.0-23.0 | cothromachadh | ≤3.0 | 15.0-17.0 | 3.0-4.5 | 1.3-1.9 | ≤0.08 | ≤0.5 | ≤0.02 | ≤0.08 |
Dùmhlachd
|
8.5 g / cm³
|
Puing leaghaidh
|
1260-1320 ℃
|
Tiugh (mm) |
Neart tensile (Mpa) | Neart toraidh σ0.2 (Mpa) |
Fadachadh (50.8mm) (%) |
1.6 | 752 | 358 | 64.0 |
3.18 | 765 | 393 | 63.0 |
6.35 | 779 | 379 | 62.0 |
12.7 | 758 | 345 | 68.0 |
25.4 | 752 | 372 | 63.0 |
ASTM B564, ASTM B574, ASTM B575, ASTM B619, ASTM B622 , ASTM B366
Bàr / Slat | Uèir | Stiall / Coil | Duilleag / Pleit | Pìob / Tiùb |
A ’cur an aghaidh creimeadh a’ toirt a-steach searbhag sulfuric hydrochloric hydrofluoric acid phosphate clorine organach alcalan meatailt creimeadh pitting, sgoltadh creimeadh cuideam.
Tha alloy C-2000 a ’nochdadh dìon nas fheàrr an aghaidh creachadh pitting agus crevice na C-276 alloy an ìre gnìomhachais.
Foirmleachadh tàthaidh is innealachaidh Hastelloy C-2000 a tha coltach ri C276, a ’fuasgladh an dileab air dealbhadh an alloy.
A ’cur an aghaidh creimeadh sàr-mhath ri àrainneachd lughdachadh gun a bhith ag ìobairt seasmhachd meatailte ann an co-bhonn le cromium àrd agus susbaint molybdenum agus copar.
• Reactair gnìomhachas pròiseas ceimigeach, iomlaid teas, colbhan agus a ’phìob.
• Reactair agus tiormaiche gnìomhachas cungaidh-leigheis.
• Siostam desulfurization gas flùr.